Parameters
-
Comments
| MGO: | 60% | Cr2O3: | 12% |
|---|---|---|---|
| Apparent Porosity: | 22% | Crushing Strength: | 45MPa |
| 0.20MPa Softening Initiation Temperature,癈: | 1700癈 |
The Fused-rebonded Refractory Magnesia Chrome Brick for Hot Blast Furnace
Description
The fused-rebonded magnesia chrome brick is made with sintered magnesia and refractory level chrome ore as raw materials. The space between refractory grains is bonded with silicate.The refractoriness of magnesia chrome bricks are more than 2000°C,and the refractory under load is a above 1550°C.Good steady volume in high temperature , the performance of meeting sudden cold and sudden hot is better than magnesia bricks.
Advantage
The fused-rebonded magnesia chrome brick has high temperature resistance, good corrosion resistance, thermal shock resistance and bulk stability under high temperature etc .
Application
The fused-rebonded magnesia chrome brick mainly used in metallurgy(open hearth,EAF), non-ferrous (metall-urgyfurnace ) , buildings and materials (cement rotary kiln,glass kiln) etc.
| Brand No. | Magnesia Composition(%) |
A.P. (%)≤ |
B.D. (g/cm3)≥ |
C.C.S MPa≥ |
0.2MPa Refractoriness Under Load(°C)≥ | |||
|
MgO (%)≥ |
SiO2 (%)≥ |
Cr2O3 (%)≥ |
||||||
|
Directly Combined MgO-Cr2O3 Brick |
RSZMG-12 | 70 | 1.5 | 12 | 17 | 3.05 | 45 | 1700 |
| RSZMG-16 | 60 | 1.5 | 16 | 18 | 3.05 | 45 | 1700 | |
| RSZMG-18 | 58 | 1.5 | 18 | 18 | 3.05 | 40 | 1700 | |
| RSZMG-20 | 55 | 1.5 | 20 | 18 | 3.05 | 40 | 1700 | |
| RSZMG-22 | 52 | 2 | 22 | 18 | 3.05 | 40 | 1700 | |
|
Fused Semi-rebond MgO-Cr2O3 Brick |
FRMGe -16 | 60 | 1.4 | 16 | 16 | 3.08 | 50 | 1700 |
| FRMGe -18 | 58 | 1.5 | 18 | 16 | 3.10 | 50 | 1700 | |
| FRMGe -20 | 55 | 1.5 | 20 | 16 | 3.15 | 50 | 1700 | |
| FRMGe -22 | 50 | 1.5 | 22 | 16 | 3.20 | 50 | 1700 | |
| FRMGe -26 | 45 | 1.5 | 26 | 16 | 3.25 | 50 | 1700 | |
|
Fused Re-bond MgO-Cr2O3 Brick |
FRMGe-12 | 68 | 1.2 | 12 | 16 | 3.00 | 50 | 1700 |
| FRMGe-14 | 65 | 1.4 | 14 | 16 | 3.05 | 50 | ||
Product Pictures: